low alloy structural steel EN 1.6587 is is a heat treatable, low alloy steel containing nickel, chromium and molybdenum as per DIN Germany standard which is known for its toughness and capability of developing high strength in the heat treated condition while retaining good fatigue strength. low alloy structural steel EN 1.6587 is widely used in heavy duty Shafts, Gears, Axles, Spindles, Couplings, Pins etc.

Low alloy structural steel EN1.6587 CHEMICAL COMPOSITION PER DIN 17210 (CASE HARDENING STEELS)

GRADE	NUMBER	C	Si	Mn	P	S	Cr	Mo	Ni
17CrNiMo6	1.6587	0.15-0.20	≤ 0.40	0.40-0.60	≤ 0.035	≤ 0.035	1.50-1.80	0.25-0.35	1.40-1.70

Low alloy structural steel EN1.6587 SIZE&TOLERANCE&PROCESS

Round	Φ6-Φ50	Cold Drawn	H11	3000-5800
Round	Φ40-Φ300	Hot Rolled	-0/+3mm	3000-10000
Round	Φ120-Φ1000	Hot Forged	-0/+3mm	3000-10000
Flat/Square/Block	Thickness:120-800 Width:120-1500	Hot Forged	-0/+3mm	500-6000

Low alloy structural steel EN1.6587 HEAT TREATMENT

Normalizing For 17CrNiMo6/1.6587
1.Nominal normalizing temperature:840-890°C
2.Hold the temperature for several hours
3.Cooling in the air

Annealing For 17CrNiMo6/1.6587
1.Nominal Annealing temperature:630-650°C
2.Cool slowly in the furance
3.Maximum Brinell hardness of 229

Hardening and Tempering(QT) For 17CrNiMo6/1.6587
1.Nominal Hardening temperature:830-865°C
2.Hold at this temperature then quench in oil
3.Tempering as soon as possible when the temperature low to ambient temperature
4.Heat the steel carefully to a suitable temperature selected by reference to a tempering chart or table
5.The usual tempering temperature is 600°C which depending on the actual requirements
6..keep the material out of the furnace ,then cool in the air

Low alloy structural steel EN1.6587 MECHANICAL PROPERTY( FOR REFERENCE ONLY)

1.Tensile strength: 980-1270MPa
2.Yield point: 780MPa
3.Percentage reduction of area after fracture: 40%
4.Elongation after fracture: 11%
5.Impact test (+20°C): Longitud – 45~50J

Low alloy structural steel EN1.6587 DELIVERY CONDITION

1.Shape:Round/Square / Flat/Shafts/Rollers/Blocks
2.Surface condition:Black surface/Bright surface
3.Heat Treatment:Normalized/Annealed/QT
4.Straightness:Max 3mm/m(Enhanced straightness may be available on request)
5.Length:3000-5800mm suitable for 20″container. above 6000mm,suitable for 40″ container
6.Grain Size: 5-8 acc to ASTM E112-96
7.Typcial Hardness:HRC28-32
8.Ultrasonic Standard: Sep1921/ASTM A388/EN 10228-3
9.Non Metallic Inclusion: 2 max acc to ASTM E45 /K4≤20 acc to DIN 50602
10.Forging Ratio: minimum 4 : 1
11.Marking: Grade/Weight/Length/Size/Heat Number

Low alloy structural steel EN1.6587 QUALITY CERTIFICATION

A material test report(Inspection Certificate EN 10204 3.1) will be provided, documenting the following:
1.Chemical analysis
2.Mechanical properties
3.Surface hardness
4.Non Metallic Inclusion
5.Heat Treatment Process
6.Grain size
7.Forging ratio
8.NDE test method/criteria

17CrNiMo6/1.6587 Steel manufacturers and suppliers, supplied with round rods,square/flat bars,rollers,shafts,blocks and forging pieces.

Populární Tagy: low alloy structural steel en1.6587, China, suppliers, manufacturers, factory, buy, price, pricelist, for sale, in stock, free sample